Re: [MW:9800] ferritic stainless steel Procedure weld crack

why dint you preferred Er-309Mol,instead of what u used??
 
 


 
On Wed, Feb 9, 2011 at 7:14 PM, krishna <wiqw@rediffmail.com> wrote:

dear guys,

                   Request to give your comments for the below


Material used for welding is SA 240 TP 410S weld over lay on carbon steel(SA 516 )


Consumable used Barrier layer -Pure iron (electrode D& H 45S)

Further layer  E 430-15 (D& H 17Cr)

Preheating temp-100:c

Interpass temp-250c


Weld overlay was done for 8mm on Carbon steel plate thickness 8mm.

After welding there was some minor distortion ,to remove distortion slight straightening was done on jack.

During starightening we noticed crack on overlay.


I want to know why crack was developed ,how to overcome this situation.

Advice what precaution to be taken to qualify this procedure.

Why the weld overlay crack developed is there any other reason.


thanks expecting you guys to reply

krishna



--
To post to this group, send email to materials-welding@googlegroups.com
To unsubscribe from this group, send email to materials-welding+unsubscribe@googlegroups.com
For more options, visit this group's bolg at http://materials-welding.blogspot.com/
The views expressed/exchnaged in this group are members personel views and meant for educational purposes only, Users must take their own decisions w.r.t. applicable code/standard/contract documents.

--
To post to this group, send email to materials-welding@googlegroups.com
To unsubscribe from this group, send email to materials-welding+unsubscribe@googlegroups.com
For more options, visit this group's bolg at http://materials-welding.blogspot.com/
The views expressed/exchnaged in this group are members personel views and meant for educational purposes only, Users must take their own decisions w.r.t. applicable code/standard/contract documents.

No comments:

Re: [MW:34832] Inquiry about Single Bevel with Back Grinding

Dear Uday, As per your question that one is called with backing only,Simple both side you are welding it is backing with strip or without st...