Re: [MW:9148] Welding of Clad Materials

Dear Mr.Karthikeyan,

Thanks for your inputs.

My question was specifically for the clad materials(Example :Stainless
steel 10mm plate Claded on 40mm Carbon steel plate)What must be
checked prior to welding.

I have got some answers from my close collegues which is as follows:

1.As an Example stated above SS Claded on CS,We need to remove the
clad material from the edges for welding ,then check the Carbon steel
edges with copper sulfide solution(Etching) to ensure all the
particles of claded material(SS) has been removed(otherwise there is a
chance for cracking).

2.Then there is precautionary step to be taken before start the
welding,that is either cover the rest of the claded surface(SS) with
Limestone powder or mask with some adhesive tapes during the welding
activity.

3.Finally do the overlay welding with correct electrode.

Kindly post if you have any corrections or suggestions on the above details.

Regards,

SURESH.
On 1/7/11, Karthik <karthik6684@yahoo.com> wrote:
> Hi,
> Iam sorry to say that you are not specific in your quirey in detail.Any how
> the simple steps are ,suitable wps,welder qualificatin,filler
> metal,cleanliness,preparation of joint(some 10mm between both side of c/s
> weld metal etc.,(these are all before start..during and after is many
> things)
> I think you are already know the basics.if you need the specific
> details,pls..give your quirey in detail.
>
> Thanks & Regards,
>
> (Karthik)
>
> Karthikeyan.S QA/QC Manager Getabec Energy Co.,Ltd.
> 379,Moo6,Soi8,Nikhomphatana, Rayong-21180, Thailand. Phone: 0066 38
> 897035-8 (Off) Fax: 0066 38 897034 Hand Phone: 0066 892512282
>
> --- On Fri, 1/7/11, Suresh Babu <suresh75.babu@gmail.com> wrote:
>
> From: Suresh Babu <suresh75.babu@gmail.com>
> Subject: [MW:9127] Welding of Clad Materials
> To: "Materials & Welding" <materials-welding@googlegroups.com>
> Date: Friday, January 7, 2011, 3:10 PM
>
> Dear Team,
>
> What is the most important to be checked before start welding of Clad
> Material?.
>
> Thanks in Advance.
> suresh.
>
> --
> To post to this group, send email to materials-welding@googlegroups.com
> To unsubscribe from this group, send email to
> materials-welding+unsubscribe@googlegroups.com
> For more options, visit this group's bolg at
> http://materials-welding.blogspot.com/
> The views expressed/exchnaged in this group are members personel views and
> meant for educational purposes only, Users must take their own decisions
> w.r.t. applicable code/standard/contract documents.
>
>
>
>
>
> --
> To post to this group, send email to materials-welding@googlegroups.com
> To unsubscribe from this group, send email to
> materials-welding+unsubscribe@googlegroups.com
> For more options, visit this group's bolg at
> http://materials-welding.blogspot.com/
> The views expressed/exchnaged in this group are members personel views and
> meant for educational purposes only, Users must take their own decisions
> w.r.t. applicable code/standard/contract documents.
>

--
To post to this group, send email to materials-welding@googlegroups.com
To unsubscribe from this group, send email to materials-welding+unsubscribe@googlegroups.com
For more options, visit this group's bolg at http://materials-welding.blogspot.com/
The views expressed/exchnaged in this group are members personel views and meant for educational purposes only, Users must take their own decisions w.r.t. applicable code/standard/contract documents.

Re: [MW:34105] SA266 GR4N 4 Cycle SPWHT

Hi, You are correct, Minimum refers to the one cycle for which this part will expose until final work shop PWHT. hence mill test certificate shall include this. Max. SPWHT, refers to additional cycles of heat treatment that are reserved for future repairs during equipment lifetime. Again, these simulated no. Of cycles shall be specified in MTC. The idea is we need to make sure that steel mechanical properties are not compromised upon exposure to multiple repairs (i e 4 cycles in your case). One could say, if steel is subjected to 4 cycles and is ok, then it should by defacto be good for one cycle, yet, this is wrong assumption cause mechanical problems and microstructure of materials varies accordingly based on no. Of cycles for which material will expose. This is apparent in alloy steel and especially for impact test values as an example. In your case, this forged CS with properties before PWHT can be understood to be " as forged" condition (i.e. Wit...

Materails FAQs

Q: What are equivalents for standard Q 235 B (and Q 235 A) for U-channels? (asked by: boris.vielhaber@vait.com) A: DIN Nr. = 2393 T.2, 2394 T.2, EN 10025 W. Nr. DIN 17007 = 1.0038 Design DIN 17006 = RSt 37-2, S235JRG2 (Fe 360 B) Q: What is St DIN 2391 BK material? (asked by: dmcandrews@automaticstamp.com) A: Precision steel tubes, cold-finished/hard. Q: What is C.D.W. Boiler Tube? (asked by: montydude123@yahoo.com) A: Cold Drawn Welded Boiler Tube. Q: WHAT IS W.Nr. 1.4301? PLS TELL US IN EASY LANGUAGUE (asked...

Heat tint (temper) colours on stainless steel surfaces heated in air // Heat tint

Introduction The colour formed when stainless steel is heated, either in a furnace application or in the heat affected zone of welds, is dependent on several factors that are related to the oxidation resistance of the steel. The heat tint or temper colour formed is caused by the progressive thickening of the surface oxide layer and so, as temperature is increased, the colours change. Oxidation resistance of stainless steels However, there are several factors that affect the degree of colour change and so there is no a single table of colour and temperature that represents all cases. The colours formed can only be used as an indication of the temperature to which the steel has been heated. Factors affecting the heat tint colours formed Steel composition The chromium content is the most important single factor affecting oxidation resistance. The higher the chromium, the more heat resistant the steel and so the development of the heat tint colou...

Materials & Welding

Search This Blog