Saturday, December 18, 2010

Re: [MW:8795] UTS

I totaly disagree with manpreet because heat input only affects the
tougness property of material. As far as i know UTS never depends on
the welding processes. BHAVESH

On 12/18/10, manpreet <manpreetsin88@rediffmail.com> wrote:
> Hi, Heat Input is goint to be the key factor in this case, which would be
> less for GTAW.so for GTAW, there would be more UTS.Due to limited
> information, this is only thing i can predict, else more info like heat
> treated condition and weld joint, would be needed.RegardsManpreet
> SinghWelding EngineerOn Fri, 17 Dec 2010 8:43:49 , Harish Kannepalli
> &lt;harishkannepalli@gmail.com&gt; wrote
> In theory both will have same UTS. But while testing, slight variation may
> be there due testing conditions.
> 2010/12/16 Shaunak Upadhyay &lt;shanupadhyay@gmail.com&gt;
> 1) &nbsp;Material Specifcaiton: SA 516 GR 70&nbsp; &nbsp; Size: 6.0 mm
> thk&nbsp; &nbsp; &nbsp; &nbsp; &nbsp; &nbsp; &nbsp;300 mm Length x 300 mm
> Width&nbsp; &nbsp; Process: GTAW&nbsp; &nbsp; Consumable: ER70S-22)
> &nbsp;Material Specifcaiton: SA 516 GR 70&nbsp; &nbsp; Size: 6.0 mm
> thk&nbsp; &nbsp; &nbsp; &nbsp; &nbsp; &nbsp; &nbsp;300 mm Length x 300 mm
> Width&nbsp; &nbsp; Process: SMAW&nbsp; &nbsp; Consumable: E7018Which test
> piece have more UTS in these two processes.Regards,Shaunak Upadhyay--To post
> to this group, send email to materials-welding@googlegroups.comTo
> unsubscribe from this group, send email to
> materials-welding+unsubscribe@googlegroups.comFor more options, visit this
> group's bolg at http://materials-welding.blogspot.com/The views
> expressed/exchnaged in this group are members personel views and meant for
> educational purposes only, Users must take their own decisions w.r.t.
> applicable code/standard/contract documents.--
>
> regards,
> Harish.
> -- To post to this group, send email to materials-welding@googlegroups.comTo
> unsubscribe from this group, send email to
> materials-welding+unsubscribe@googlegroups.comFor more options, visit this
> group's bolg at http://materials-welding.blogspot.com/The views
> expressed/exchnaged in this group are members personel views and meant for
> educational purposes only, Users must take their own decisions w.r.t.
> applicable code/standard/contract documents.
>
> --
> To post to this group, send email to materials-welding@googlegroups.com
> To unsubscribe from this group, send email to
> materials-welding+unsubscribe@googlegroups.com
> For more options, visit this group's bolg at
> http://materials-welding.blogspot.com/
> The views expressed/exchnaged in this group are members personel views and
> meant for educational purposes only, Users must take their own decisions
> w.r.t. applicable code/standard/contract documents.
>

--
To post to this group, send email to materials-welding@googlegroups.com
To unsubscribe from this group, send email to materials-welding+unsubscribe@googlegroups.com
For more options, visit this group's bolg at http://materials-welding.blogspot.com/
The views expressed/exchnaged in this group are members personel views and meant for educational purposes only, Users must take their own decisions w.r.t. applicable code/standard/contract documents.

No comments:

Re: [MW:34832] Inquiry about Single Bevel with Back Grinding

Dear Uday, As per your question that one is called with backing only,Simple both side you are welding it is backing with strip or without st...