Re: [MW:8696] yielld strength for SA 387 GR 12 CL2 80 THK TEST COUPON

Hi!
Basically mechanical properties depends upon Chemistry of plate (Base metal) particularaly C % Mo % and subsequent heat treatment
Generaly With Qn + Tempering condition gives better mechanical properties copared to NR + Tempering
 
With 4 PWHT cycle, generaly UTS reduces and subsequently YS also ,in such case you may require to increase C% (Higher side of acceptable range) In your case you have to get confirmation from Mill,
 as my experience, mill is reluctant to give suitable plate with 4 PWHT that to at 690C -700C with plate under NR +Temper condition
 
Regards
 
Hegde P.B.


From: asad azmi <azmiasadayub@gmail.com>
To: materials-welding@googlegroups.com
Sent: Sat, 11 December, 2010 12:37:57 PM
Subject: [MW:8688] yielld strength for SA 387 GR 12 CL2 80 THK TEST COUPON

Dear All,
 
Greetings.
 
shell plate material :  SA 387 GR 12 CL2  80 THK  Delivery Condition :  noramlized + tempered.
 
Please inform me whether Yield strength will increase OR Decrease after further heat treatmen in 2 conditions Detailed as below.
 
1) after re normalizing + re temperting
 
2) after re normalizing + re temperting +  4 pwht cycles
 
regards
 
asad azmi
 

--
To post to this group, send email to materials-welding@googlegroups.com
To unsubscribe from this group, send email to materials-welding+unsubscribe@googlegroups.com
For more options, visit this group's bolg at http://materials-welding.blogspot.com/
The views expressed/exchnaged in this group are members personel views and meant for educational purposes only, Users must take their own decisions w.r.t. applicable code/standard/contract documents.

No comments:

Re: [MW:34832] Inquiry about Single Bevel with Back Grinding

Dear Uday, As per your question that one is called with backing only,Simple both side you are welding it is backing with strip or without st...