[MW:8991] RE: 8989] E -7018 (TAPPER BURNING)

Dear Jignesh,

 

The possible reasons are:

1)      Manufacturing defect i.e the flux coating and the core wire are not concentric that leads to excess coating at once side

2)      The core wire is not straightened properly in the manufacturing process.

3)      Influence of magnetic flux in the welding area which gives arc blow that gives a feeling of one-side burning.

 

Regards,

Shankar Narayan

 

 

From: materials-welding@googlegroups.com [mailto:materials-welding@googlegroups.com] On Behalf Of Jignesh Desai
Sent: Wednesday, December 29, 2010 8:33 PM
To: materials-welding@googlegroups.com
Subject: [MW:8989] E -7018 (TAPPER BURNING)

 

Can anybody write some technical reasons behind tapper burning of subject electrodes with high fluctuations of current and wastage of excessive stub length because of red hot (@ 30%)?

 

Also with above, what could be the possible defects in the weld joints?

 

Regds/Jignesh

--
To post to this group, send email to materials-welding@googlegroups.com
To unsubscribe from this group, send email to materials-welding+unsubscribe@googlegroups.com
For more options, visit this group's bolg at http://materials-welding.blogspot.com/
The views expressed/exchnaged in this group are members personel views and meant for educational purposes only, Users must take their own decisions w.r.t. applicable code/standard/contract documents.

No comments:

Re: [MW:34832] Inquiry about Single Bevel with Back Grinding

Dear Uday, As per your question that one is called with backing only,Simple both side you are welding it is backing with strip or without st...