Zinc is sprayed on base metals by the help of arc spray process hence
ideally if you have to compare hot dip galvanizing vs thermal zinc
spray we will have to compare arc spray as a process vis-a-vis hot dip
galvanizing
Hot dip galvanizing is a process where steel or even aluminium is
passed thru a molten bath of zinc at a temperature of 460 degree
celsius.In this process coated zinc reacts with oxygen forming zinc
oxide which further reacts with CO2 to form Zinc carbonate which
increases the corrosion resistance of parts coated.
Arc spray is a process wherein two wires melt with a arc and the
molten pool is sprayed on the substrate by the help of compressed
air.
Now both the above processes come with their own advantages and
disadvantages. Arc spray can be done quickly and is a viable option
for smaller parts while Hot dip galvanizing is good for bigger
parts . Arc spray coatings will have inherent porosity while hot dip
coatings will be smoother. Arc spray coatings have thickness advantage
and can be done for higher thickness of coating while hot dip doesnt
qualify in such cases.
Weldbro
Weldbro blogs regularly at www.weldblog.com which is the first and
most vibrant dedicated blog of welding community and invites all to
participate. You can even apply to be a author with full control on
your articles.
Best Regards
On Dec 9, 8:44 pm, Arun Das <indhua...@yahoo.co.in> wrote:
>
> Dear Mr.Hegde,
>
> Thermal spray coatings are a melted, or softened ceramic, metallic, or polymer
> materials are transported by a gas stream to a properly prepared substrate
>
> Hot-dip galvanizing is essentially a brazing process. Steel is cleaned
> (mechanically and chemically) and then heated to >850°F in a molten zinc bath.
> The molten zinc reacts with the surface of the steel and forms a coating of
> various layers of zinc and iron alloys, depositing a layer of material that is
> approximately 40% pure zinc.
>
> Arun S Das
> Inspection Engineer
> Velosi Certification LLC
> Qatar
> Mob: +97433240549 +97433240549 +919847051202 +919847051202( India )
>
> ________________________________
> From: Qamlr <qa...@cicb-chemicon.com>
> To: "materials-welding@googlegroups.com" <materials-welding@googlegroups.com>
> Sent: Thu, 9 December, 2010 2:24:58 PM
> Subject: [MW:8627] Hot dip galvanising Vs thermal zinc spray
>
> Dear Team members
>
> Could you please explain basic difference between hot dip galvanizing and
> thermal zinc spray. We have requirement of both on certain component. Can I
> adopt thermal zinc spray process in lieu of hot dip galvansing.
>
>
> Please clarify.
>
> Regards
>
> Prashanth Hegde
> ________________________________
> Please don't print this e-mail unless you really need to.
> *******************************************************************
> This e-mail is confidential. It may also be legally privileged. If you are not
> the addressee you may not copy, forward, disclose or use any part of it. If you
> have received this message in error, please delete it and all copies from your
> system and notify the sender immediately by return e-mail. Internet
> communications cannot be guaranteed to be timely, secure, error or virus-free.
> The sender does not accept liability for any errors or omissions.
> *******************************************************************
> "SAVE PAPER - THINK BEFORE YOU PRINT!"
> --
> To post to this group, send email to materials-welding@googlegroups.com
> To unsubscribe from this group, send email to
> materials-welding+unsubscribe@googlegroups.com
> For more options, visit this group's bolg athttp://materials-welding.blogspot.com/
> The views expressed/exchnaged in this group are members personel views and meant
> for educational purposes only, Users must take their own decisions w.r.t.
> applicable code/standard/contract documents.
--
To post to this group, send email to materials-welding@googlegroups.com
To unsubscribe from this group, send email to materials-welding+unsubscribe@googlegroups.com
For more options, visit this group's bolg at http://materials-welding.blogspot.com/
The views expressed/exchnaged in this group are members personel views and meant for educational purposes only, Users must take their own decisions w.r.t. applicable code/standard/contract documents.
No comments:
Post a Comment