protection and are metallurgical bonds basic difference is in case of
zink spray there is a possibility of porosity which is not in case of
HDG the porosity level could be 6 yo 7 % in case of flame spray and 2
to 3% in case of arc spray
On Dec 9, 1:54 pm, Qamlr <qa...@cicb-chemicon.com> wrote:
> Dear Team members
>
> Could you please explain basic difference between hot dip galvanizing and thermal zinc spray. We have requirement of both on certain component. Can I adopt thermal zinc spray process in lieu of hot dip galvansing.
>
> Please clarify.
>
> Regards
>
> Prashanth Hegde
>
> ________________________________
> Please don't print this e-mail unless you really need to.
> *******************************************************************
> This e-mail is confidential. It may also be legally privileged. If you are not the addressee you may not copy, forward, disclose or use any part of it. If you have received this message in error, please delete it and all copies from your system and notify the sender immediately by return e-mail. Internet communications cannot be guaranteed to be timely, secure, error or virus-free. The sender does not accept liability for any errors or omissions.
> *******************************************************************
> "SAVE PAPER - THINK BEFORE YOU PRINT!"
--
To post to this group, send email to materials-welding@googlegroups.com
To unsubscribe from this group, send email to materials-welding+unsubscribe@googlegroups.com
For more options, visit this group's bolg at http://materials-welding.blogspot.com/
The views expressed/exchnaged in this group are members personel views and meant for educational purposes only, Users must take their own decisions w.r.t. applicable code/standard/contract documents.
No comments:
Post a Comment