Re: [MW:7997] LM parameters

Thanks for literature of Dillinger on HP parameter
 
However I want to know how many time we can Normlise (Heat the  CS plate above AC3 ) during hot rolling the plate (During hot forming of shell)
 
with out affecting themechanical  properties
 
Regards
 
Hegde P.B.


From: Bathula Raghuram (Mumbai - PIPING) <R.Bathula@ticb.com>
To: "materials-welding@googlegroups.com" <materials-welding@googlegroups.com>
Sent: Mon, 1 November, 2010 5:15:53 PM
Subject: RE: [MW:7995] LM parameters

Thou I am not clear with this parameter, attached document might be helpful to you,

 

HP: You can calculate online @ dillinger.de

 

 

From: materials-welding@googlegroups.com [mailto:materials-welding@googlegroups.com] On Behalf Of Prakash Hegde
Sent: Monday, November 01, 2010 5:00 PM
To: materials-welding@googlegroups.com
Subject: [MW:7993] LM parameters

 

Requested to share your view

Regarding --LM parameter /HP parameter

While calculating total equvilalent heat treatment time through LM parameters Do we require to consider Normalising time also ?

Can we apply LM parameter for Normalising cycle also similar to Heat treatment below AC1 temp.

 

Regards

 

Hegde P.B.

 


--
To post to this group, send email to materials-welding@googlegroups.com
To unsubscribe from this group, send email to materials-welding+unsubscribe@googlegroups.com
For more options, visit this group's bolg at http://materials-welding.blogspot.com/
The views expressed/exchnaged in this group are members personel views and meant for educational purposes only, Users must take their own decisions w.r.t. applicable code/standard/contract documents.

No comments:

Re: [MW:34832] Inquiry about Single Bevel with Back Grinding

Dear Uday, As per your question that one is called with backing only,Simple both side you are welding it is backing with strip or without st...