Dear Roy,
Pl, conform tp P91 by PMI.Because, I have also china customer
& their composition is different from ASTM/BIS.
Review PQR once again.
Thanks,
With Warm Regards,
Keep in touch,
K.NANDAGOPAL;
09977729258
09360049258-
From: materials-welding@googlegroups.com [mailto:materials-welding@googlegroups.com] On Behalf Of Roy LIU??
Sent: Sunday, November 14, 2010 6:00 PM
To: materials-welding@googlegroups.com
Subject: [MW:8258] How to control cracks when weld P91 and P91
Dear All,
I just meet a problem from one of my customers.
It is a Boiler Manufactory in China.
Details as follow:
base material: P91
process: SMAW (root) + SAW (filler metals)
Heat Input: high
I=380A
U=35V
V=250mm/min
Preheat, Interpass Temperature: ≤250℃
How to control cracks?
How to increase impact properties afer PWHT?
Best regards
Roy LIU
--
To post to this group, send email to materials-welding@googlegroups.com
To unsubscribe from this group, send email to materials-welding+unsubscribe@googlegroups.com
For more options, visit this group's bolg at http://materials-welding.blogspot.com/
The views expressed/exchnaged in this group are members personel views and meant for educational purposes only, Users must take their own decisions w.r.t. applicable code/standard/contract documents.
No comments:
Post a Comment