[MW:8258] How to control cracks when weld P91 and P91

Dear All,
I just meet a problem from one of my customers.
It is a Boiler Manufactory in China.
 
Details as follow:
base material: P91
process: SMAW (root) + SAW (filler metals)
Heat Input: high  
I=380A
U=35V
V=250mm/min
Preheat, Interpass Temperature: ≤250℃
 
How to control cracks?
How to increase impact properties afer PWHT?


 

Best regards

 

Roy LIU

By -

No comments:

Post a Comment

Subscribe to: Post Comments (Atom)

Re: [MW:34913] Filler wire

E71T-1C  is Charpy Impact tested at -20degC E71T-1CJ is Charpy impact tested at -40degC. AWS Classification for FCAW is only a supplementary...

  • Materails FAQs
    Q: What are equivalents for standard Q 235 B (and Q 235 A) for U-channels? ...
  • RE: [MW:5585] Buttering of weld joints
    Definition of buttering from ASME Section IX, QW/QB-492 Definitions:   Buttering:  the addition of material, by welding, on one or bot...
  • WELD AND WELDING SYMBOLS
    Section I. PRINT READING 3-1. GENERAL a. Drawings . Drawing or sketching is a universal language used to convey all necessary information to...