On Wed, Oct 13, 2010 at 12:13 PM, santosh bhandary <sancraze_2000@yahoo.co.in> wrote:
- Preheat temperature
- PWHT
- Electrical characteristics
--- On Wed, 6/10/10, muthusrinivasan muthuselvam <msms2k@gmail.com> wrote:
From: muthusrinivasan muthuselvam <msms2k@gmail.com>
Subject: Re: [MW:7390] Post Heating for Alloy SteelDate: Wednesday, 6 October, 2010, 11:47 AM
Mr.Senthil..The main purpose of doing immediate PWHT without post heating is to avoid hydrogen induced cracking.. To my knowledge there is no code requirement or specification mentioning about the time after which you can do the PWHT.But please note that delaying the PWHT after welding will improve the condition for hydrogen induced cold cracking. So the PWHT has to be carrried out immediately after completion of welding.best regards,M.S.Muthu selvam.On Tue, Oct 5, 2010 at 10:42 PM, senthil raja <senthilrajabarathi@gmail.com> wrote:
Hi,
I m Senthil working in L&T. I m presently in MRPL project,
Mangalore. In our client(EIL) specification it is given that post
heating shall be carried out for the alloy steels (Cr-Mo) where PWHT
cannot be carried out immediately.
I need to know what is the time limit within which PWHT shall be
carried out without post heating. What is the standard or code which
can be reffered for this.
Kindly share your experience sirs & friends,
regards,
Senthil Raja.
--
To post to this group, send email to materials-welding@googlegroups.com
To unsubscribe from this group, send email to materials-welding-unsubscribe@googlegroups.com
For more options, visit this group's bolg at http://materials-welding.blogspot.com/
The views expressed/exchnaged in this group are members personel views and meant for educational purposes only, Users must take their own decisions w.r.t. applicable code/standard/contract documents.
--
To post to this group, send email to materials-welding@googlegroups.com
To unsubscribe from this group, send email to materials-welding-unsubscribe@googlegroups.com
For more options, visit this group's bolg at http://materials-welding.blogspot.com/
The views expressed/exchnaged in this group are members personel views and meant for educational purposes only, Users must take their own decisions w.r.t. applicable code/standard/contract documents.
--To post to this group, send email to materials-welding@googlegroups.com
To unsubscribe from this group, send email to materials-welding-unsubscribe@googlegroups.com
For more options, visit this group's bolg at http://materials-welding.blogspot.com/
The views expressed/exchnaged in this group are members personel views and meant for educational purposes only, Users must take their own decisions w.r.t. applicable code/standard/contract documents.
--
This message originated from the Internet. Its originator may or may not be who they claim to be and the information contained in the message and any attachments may or may not be accurate.
This email transmission is intended solely for the named recipient(s). It may contain confidential and/or privileged information.If you are not the intended recipient, note that disclosing, copying or distributing it may be unlawful. Please notify the sender immediately if you have received it by mistake, and delete it from your system.
Internet communications cannot be guaranteed to be timely, secure, error or virus-free. The sender does not accept liability for any errors or omissions.
"SAVE PAPER - THINK BEFORE YOU PRINT!"
Regards,
~ DEVARAJAN RAMASAMY~
--
To post to this group, send email to materials-welding@googlegroups.com
To unsubscribe from this group, send email to materials-welding-unsubscribe@googlegroups.com
For more options, visit this group's bolg at http://materials-welding.blogspot.com/
The views expressed/exchnaged in this group are members personel views and meant for educational purposes only, Users must take their own decisions w.r.t. applicable code/standard/contract documents.
No comments:
Post a Comment