What was the thickness of weld joint?
vanchi
On Fri, Oct 8, 2010 at 9:35 PM, Srini <sethu.srini@gmail.com> wrote:
Hello, Need some help here.
Pqr was developed with GMAW STT root and FCAW fill. Filler metals were
ER2209 and E2209T1-4.
Shielding gas Mison 2C (98+2Co2) for STT, Mison 25C (98+25Co2) for
FCAW. Impacts, Corrosion per A923 Method C passed. However when
metallographically tested for ferrite count per ASTM E562 we found the
ferrite content in root HAZ was as high as 69 - 70%. Typically we
would like to achieve 60 or 65% for better corrosion properties. Heat
input root pass= 25Kj/inch and fill passes=35Kj/inch. Backing gas was
100%Ar.
Any suggestions for reducing the ferrite content in HAZ of root is
welcome. Thanks in advance.
Srini
--
To post to this group, send email to materials-welding@googlegroups.com
To unsubscribe from this group, send email to materials-welding-unsubscribe@googlegroups.com
For more options, visit this group's bolg at http://materials-welding.blogspot.com/
The views expressed/exchnaged in this group are members personel views and meant for educational purposes only, Users must take their own decisions w.r.t. applicable code/standard/contract documents.
--
To post to this group, send email to materials-welding@googlegroups.com
To unsubscribe from this group, send email to materials-welding-unsubscribe@googlegroups.com
For more options, visit this group's bolg at http://materials-welding.blogspot.com/
The views expressed/exchnaged in this group are members personel views and meant for educational purposes only, Users must take their own decisions w.r.t. applicable code/standard/contract documents.
No comments:
Post a Comment