For Practice C : 5 x 48 hours means one sample which need to be tested
for 5 periods of 48 hours. After every single period the test solution
need to be refreshed and the samples weight need to be measured.
For Practice E: Acceptance criteria --> cracks present in the specimen
after bending (visible with eye and/or microscopic) are not
acceptable. Only small cracks started from the specimens corners may
left outside the examination. By bending the specimen you can prove
that grain boundaries are not affected due to corrosion.
Hope this clears everything a little bit more.
Best Regards,
Herman
On 19 sep, 06:21, limesh M <limes...@gmail.com> wrote:
> Dear Herman Sir,
>
> Thank you for the valuable information .I need some clarification on the
> following lines.
>
> "Practice C (Huey) = Standard 5 x 48 hours" , what is this 5? 5 pieces of
> test specimen or any other item?
>
> "Practice E (Strauss) = Standard is 15 hours - Boiling Acidified Copper
> Sulfate Test Solution (if required also 48 or 72 hours can be used),
> acceptance criteria are cracks in the specimen after three point bend
> test."
>
> Acceptance criteria are cracks or no cracks?If answer is cracks,then what is
> the logic behind that?
>
> Please clear my dobts.
>
> Regards,
>
> Limesh
>
>
>
> On Sun, Sep 19, 2010 at 3:18 AM, hpi001 <pieper-...@kpnmail.nl> wrote:
> > Dear Limesh,
>
> > As already mentioned by Mr. Raghuram Bathula you have several tests
> > according to ASTM A262. All are related to inter-granular attack but
> > in different environments. Find below the solutions, test time and
> > acceptance criteria for your info. Be aware that for Practice B and C
> > the max. allowable corrosion rate should be specified by your client.
>
> > Practice B (Streicher) = 1 x 120 hours Boiling Ferric Sulfate–Sulfuric
> > Acid Test Solution, acceptance criteria is corrosion rate in mm/month
> > Practice C (Huey) = Standard 5 x 48 hours - Boiling Nitric Acid Test
> > Solution (sometimes also 1 x 48 hour + 1x 96 hour is used), acceptance
> > criteria is corrosion rate in mm / month
> > Practice E (Strauss) = Standard is 15 hours - Boiling Acidified Copper
> > Sulfate Test Solution (if required also 48 or 72 hours can be used),
> > acceptance criteria are cracks in the specimen after three point bend
> > test.
>
> > Best Regards,
>
> > Herman Pieper
>
> > On 18 sep, 12:32, limesh M <limes...@gmail.com> wrote:
> > > *Dear All,*
> > > **
> > > *What is Huey test ?*
> > > **
> > > *Huey test and intergranular corrosion test as per ASTM A262 are same or
> > not
> > > ?*
> > > **
> > > *How we are finding the Intergranular corrosion?*
> > > **
> > > *What is the acceptance criteria?*
>
> > > Regards,
>
> > > Limesh
>
> > --
> > To post to this group, send email to materials-welding@googlegroups.com
> > To unsubscribe from this group, send email to
> > materials-welding-unsubscribe@googlegroups.com
> > For more options, visit this group's bolg at
> >http://materials-welding.blogspot.com/
> > The views expressed/exchnaged in this group are members personel views and
> > meant for educational purposes only, Users must take their own decisions
> > w.r.t. applicable code/standard/contract documents.
--
To post to this group, send email to materials-welding@googlegroups.com
To unsubscribe from this group, send email to materials-welding-unsubscribe@googlegroups.com
For more options, visit this group's bolg at http://materials-welding.blogspot.com/
The views expressed/exchnaged in this group are members personel views and meant for educational purposes only, Users must take their own decisions w.r.t. applicable code/standard/contract documents.
No comments:
Post a Comment