[MW:6932] P11 & P22 Hardness Issue

We are facing one serious concern regarding PWHT of weld joints of A335 Grade P11 & P22 piping in very high pressure superheated steam and syn gas service. Due to some unforeseen circumstances at our site, PWHT of some weld joints was not done effectively and resulted in higher hardness of weld joints although HAZ area hardness values are OK. The hardness number of weld joints is in the range of 260 - 320 HB which is unacceptable as per code requirements.

I want to seek expert opinion on the following:

1. Can we take these weld joints is operation and defer PWHT for planned Outage in April 2010?

2. Is there any relaxation which can be taken in hardness readings, for example, welds with hardness up to 260 may be accepted and above this number must be PWHT again?

3. What effects can it cause after taking these weld joints in service? Weld failure can occur immediately or would take some time?

4. As HAZ area hardness number is standing in the range of 115 - 150, would repeating PWHT effect this number and further reduce the hardness of HAZ which may not be acceptable?

Your inputs would definitely help me in making a correct decision.

 

Regards,

Ashfaq

 

--
To post to this group, send email to materials-welding@googlegroups.com
To unsubscribe from this group, send email to materials-welding-unsubscribe@googlegroups.com
For more options, visit this group's bolg at http://materials-welding.blogspot.com/
The views expressed/exchnaged in this group are members personel views and meant for educational purposes only, Users must take their own decisions w.r.t. applicable code/standard/contract documents.

No comments:

[MW:34820] RE: 34813] Clarification in Rate of heating and cooling.

Hello,   Please see the response below.   Regards.   P. Goswami, P. Eng, IWE.   From: materials-welding@googlegroups.com <materials-weld...