There is no other material to be welded.
 
We are working over Turbine's casing and we found those damages you can see on attached pictures.
 
By metalography we know they were fabricated on A-216 WCB and A-217 WC9
 
We appreciate your comments and suggestions
L. Carlos Flores
Piping Team Leader
Oficina:(993) 310 8100 Ext. 106
Celular:(993) 250 6610



 

From: pgoswami@quickclic.net
To: materials-welding@googlegroups.com
Subject: [MW:6789] MW: 6788- A 217 Gr WC9
Date: Mon, 30 Aug 2010 22:35:33 -0400

Hi Luis,
The material is 2.25Cr-1Mo steel (P 5A Gr 1)  in the shape of casting. What' the other material to be welded? A rule of thumb could be :-
  • A 217 Gr WC9 to P4 material-- Use P4 matching electrode for buttering, e.g-E 8018/16 B2 or E-7018B2 or GTAW filler of equivalent specification. You may use E-9018B3 or 8018B3L also, in that case buttering sequence may not be needed.
 
  • A 217 Gr WC9 to S.S- Use Inconel-182(E NiCrFe-3) or matching GTAW filler(ERNiCr-3) for buttering.PWHT the buttered area and   P5 steel as recommended by design code followed by welding to P8 without further PWHT.
Note the above guidelines are only generalized rule. Buttering sequences and welding electrodes to be used would depend on what material gets welded to A 217 Gr WC9 and the code or specification requirements.
 
Note the  precautions and welding parameters to be followed for buttering shall be identical to a groove  weld.
 
Thanks.
 
Pradip Goswami,P.Eng.
Welding & Metallurgical Engineer/Specialist
Ontario Power Generation Inc.
Email-pgoswami@sympatico.ca,
pgoswami@quickclic.net

-----Original Message-----
From: materials-welding@googlegroups.com [
mailto:materials-welding@googlegroups.com] On Behalf Of Luis Carlos
Sent: Monday, August 30, 2010 12:37 PM
To: Materials & Welding
Subject: [MW:6788] A 217 Gr WC9

Hello,

Could someone tell me please what is the best filler metal to make a buttering over A-217 Gr WC9 base metal.

Are there special recommendations?

I will appreciate answers!

Luis Carlos


--
To post to this group, send email to materials-welding@googlegroups.com
To unsubscribe from this group, send email to materials-welding-unsubscribe@googlegroups.com
For more options, visit this group's bolg at http://materials-welding.blogspot.com/
The views expressed/exchnaged in this group are members personel views and meant for educational purposes only, Users must take their own decisions w.r.t. applicable code/standard/contract documents.

--
To post to this group, send email to materials-welding@googlegroups.com
To unsubscribe from this group, send email to materials-welding-unsubscribe@googlegroups.com
For more options, visit this group's bolg at http://materials-welding.blogspot.com/
The views expressed/exchnaged in this group are members personel views and meant for educational purposes only, Users must take their own decisions w.r.t. applicable code/standard/contract documents.

No comments:

[MW:34820] RE: 34813] Clarification in Rate of heating and cooling.

Hello,   Please see the response below.   Regards.   P. Goswami, P. Eng, IWE.   From: materials-welding@googlegroups.com <materials-weld...