Mr. Elshan,

As per my experience thease ABS grade materials are for plate, for
Pipe you can use API 5L Ge X 52Z SR 18,
If pipe is fabricated by plate u can use EN 10025 S 355 K2G3 Material.

On Jul 13, 4:19 am, "pgoswami" <pgosw...@quickclic.net> wrote:
> Elshan,
>
> It's very difficult to get information on steels of  ABS specifications as
> they're proprietary. However I dug out these information. Let me know if
> your project involves:-
>
> .         The same ABS specifications
>
> .         Is it the same AH36 material, you're talking about.
>
> .         Would it be convenient from your end to email the applicable
> part/portions of ABS specs.
>
>  I am asking the above in order  to make sure that I would be able to advice
> on the correct spec and materials.
>
> Thanks.
>
> Pradip Goswami,P.Eng.
>
> Welding & Metallurgical Engineer/Specialist
>
> Ontario Power Generation Inc.
>
> Email-pgosw...@sympatico.ca <mailto:sympatico.capgosw...@quickclic.net> ,
>
> pgosw...@quickclic.net
>
> From: Elshan Feyzullayev [mailto:elsha...@hotmail.com]
> Sent: Monday, July 12, 2010 1:12 AM
> To: pgosw...@quickclic.net
> Subject: RE: ASTM A106/API5L X 52 pipe to use instead ABS AH36/dh36
>
> Hi Pradip,
>
> No it is not resolved yet. Could you please advise? And I would like to know
> what is the role of yield strength on structural and piping construction?
>
> many thanks in advance.
>
> Elshan.
>
>   _____  
>
> From: pgosw...@quickclic.net
> To: elsha...@hotmail.com
> Subject: RE: ASTM A106/API5L X 52 pipe to use instead ABS AH36/dh36
> Date: Sun, 11 Jul 2010 22:15:35 -0400
>
> Hi Elshan,
>
> I missed your email. Is this problem resolved, if not I can dig out the
> information for you.
>
> Appreciate your response.
>
> Thanks
>
> Pradip Goswami,P.Eng.
>
> Welding & Metallurgical Engineer/Specialist
>
> Ontario Power Generation Inc.
>
> Email-pgoswami@ <mailto:sympatico.capgosw...@quickclic.net> sympatico.ca,
>
> pgosw...@quickclic.net
>
>   _____  
>
> From: Elshan Feyzullayev [mailto:elsha...@hotmail.com]
> Sent: Tuesday, June 08, 2010 12:44 AM
> To: pgosw...@quickclic.net
> Subject: ASTM A106/API5L X 52 pipe to use instead ABS AH36/dh36
>
> Dear Pradip,
>
> I have got the project here a fabrication of the structural platform. The
> pipe supports are required to be ABS AH36/DH 36 which is minimum yield
> strength is required to be 355 MpA.
>
> Can we substitute this structural pipe with ASTM A106 Gr B/ASTM A333/API 5L
> X52 pipe?
>
> Could you please be so kind to give me a detailed information about it?
>
> Thank you in advance.
>
> Best regards,
> Elshan Feyzullayev.
> Baku, azerbaijan.
>
>   _____  
>
> Hotmail: Free, trusted and rich email service. Get it now.
> <https://signup.live.com/signup.aspx?id=60969>  
>
>   _____  
>
> Your E-mail and More On-the-Go. Get Windows Live Hotmail Free. Sign up now.
> <https://signup.live.com/signup.aspx?id=60969>  
>
>   _____  
>
> THIS MESSAGE IS ONLY INTENDED FOR THE USE OF THE INTENDED RECIPIENT(S) AND
> MAY CONTAIN INFORMATION THAT IS PRIVILEGED, PROPRIETARY AND/OR CONFIDENTIAL.
> If you are not the intended recipient, you are hereby notified that any
> review, retransmission, dissemination, distribution, copying, conversion to
> hard copy or other use of this communication is strictly prohibited. If you
> are not the intended recipient and have received this message in error,
> please notify me by return e-mail and delete this message from your system.
> Ontario Power Generation Inc.
>
>  ABS Part-2 - Material and Welding-Extract.pdf
> 183KViewDownload

--
To post to this group, send email to materials-welding@googlegroups.com
To unsubscribe from this group, send email to materials-welding-unsubscribe@googlegroups.com
For more options, visit this group's bolg at http://materials-welding.blogspot.com/
The views expressed/exchnaged in this group are members personel views and meant for educational purposes only, Users must take their own decisions w.r.t. applicable code/standard/contract documents.

No comments:

[MW:34820] RE: 34813] Clarification in Rate of heating and cooling.

Hello,   Please see the response below.   Regards.   P. Goswami, P. Eng, IWE.   From: materials-welding@googlegroups.com <materials-weld...