RE: [MW:5718] Using E6010+E6018 for SA 333 Gr.3

Dear All,

 

The equivalent filler rod for welding of 3.25 % Ni steels is ER80S-Ni3 and electrode E8018-C2. Refer to ASME Sec. II C, SFA 5.28- A 7.10 (Ed. 2007).

 

Regards,

 

L. Prabhu kumar,

Sr. Principal Engineer,

 

Equipments & Materials Dept.,

Saipem India Projects Limited,

Nungambakkam High Road, Chennai - 600 034, India.

Tel:+91 44 43906588, Ext.: 588, Fax:+91 44 66840345,

Mobile Ph. No.: +91 9003010978.


From: materials-welding@googlegroups.com [mailto:materials-welding@googlegroups.com] On Behalf Of v dhinesh
Sent: Tuesday, June 22, 2010 5:45 PM
To: materials-welding@googlegroups.com
Subject: Re: [MW:5705] Using E6010+E6018 for SA 333 Gr.3

 

Dear Mr.Prasad,

Thanks for your feed back. But which electrode we use for the root.

Regards,

DHINESH

On Tue, Jun 22, 2010 at 9:50 AM, N VENKATESWARA PRASAD <weldengr.velosi@gmail.com> wrote:

Dear Dhinesh,

 

SA 333 Gr.3 ( 3.5 Ni alloy steel) is  low temperature steel  used upto - 100 C which comes under P 9 group and electrode used shall be E 8018 C2.   E 6013 and E 6018 are not at all suibtable for welding of the above material.

 

regards.

N.V. PRASAD

WELDING ENGINEER

VELOSI CERTIFICATION

On Mon, Jun 21, 2010 at 1:25 PM, dhinesh <dhineshsir@gmail.com> wrote:

Dear All,

        I would like to understand what are the causes appear if you
weld the material SA 333 Gr.3 using the electrodes E6010 + E6018. I

any possibilities these electrodes acceptable to weld SA 333 Gr.3.

Regards,

DHINESH

--
To post to this group, send email to materials-welding@googlegroups.com
To unsubscribe from this group, send email to materials-welding-unsubscribe@googlegroups.com
For more options, visit this group's bolg at http://materials-welding.blogspot.com/
The views expressed/exchnaged in this group are members personel views and meant for educational purposes only, Users must take their own decisions w.r.t. applicable code/standard/contract documents.

 

--
To post to this group, send email to materials-welding@googlegroups.com
To unsubscribe from this group, send email to materials-welding-unsubscribe@googlegroups.com
For more options, visit this group's bolg at http://materials-welding.blogspot.com/
The views expressed/exchnaged in this group are members personel views and meant for educational purposes only, Users must take their own decisions w.r.t. applicable code/standard/contract documents.

 

--
To post to this group, send email to materials-welding@googlegroups.com
To unsubscribe from this group, send email to materials-welding-unsubscribe@googlegroups.com
For more options, visit this group's bolg at http://materials-welding.blogspot.com/
The views expressed/exchnaged in this group are members personel views and meant for educational purposes only, Users must take their own decisions w.r.t. applicable code/standard/contract documents.

 

 




-------------------------------------------------------------------------------------------------------------------------------------------------------------------
DISCLAIMER: The information contained in this communication is intended solely for the use of the individual or 
entity to whom it is addressed and others authorized to receive it. It may contain confidential or legally privileged 
information. If you are not the intended recipient, you are hereby notified that any disclosure, copying, distribution 
or taking any action in reliance on the contents of this information is strictly prohibited and may be unlawful. If 
you have received this communication in error, please notify us immediately by responding to this email and then 
delete it from your system. Saipem India Projects Limited (SIPL) is neither liable for the proper and complete 
transmission of the information contained in this communication nor for any delay in its receipt. 
-------------------------------------------------------------------------------------------------------------------------------------------------------------------

No comments:

Blog Archive