Micro: Needle Like structure
Hardness: 300 to 350 VHN
Regards,
From:
Sent: 08 June 2010 01:51
To:
Subject: [MW:5437] Hardness of Untempered Martensite
Hi
Any body have the idea on hardness for the untempered Martensite ?
What will be the morphology of micro?
Thanks & Regards,
K.Babu
*** WORLEYPARSONS GROUP NOTICE *** "This email is confidential. If you are not the intended recipient, you must not disclose or use the information contained in it. If you have received this email in error, please notify us immediately by return email and delete the email and any attachments. Any personal views or opinions expressed by the writer may not necessarily reflect the views or opinions of any company in the WorleyParsons Group of Companies."