[MW:3653] RE: 3647] RE: 3645] RE: 3644] Breesh-Lock Heat Exchangers Weld overlay

Hello mr Singh

Please be careful to chose ES-process if surface will be machined (indications at overlap).
Please be careful with ES high speed solution for 4,5 mm thickness in single layer : in this thickness cladding with a 24.12LNb strip the dilution will be relative low which will result in relative high ferrite contents which can be over 10%.

Please contact for accurate advise/solution directly a producer of strip cladding flux like OERLIKON / AIR LIQUIDE WELDING  

With kind regards,
Erwin GERING erwin.gering@airliquide.com
Corporate Product Manager SAW/ES wire/flux/strip
AIR LIQUIDE WELDING

-----Oorspronkelijk bericht-----
Van: materials-welding@googlegroups.com [mailto:materials-welding@googlegroups.com] Namens PB HEGDE
Verzonden: vrijdag 13 november 2009 13:17
Aan: materials-welding@googlegroups.com
Onderwerp: [MW:3647] RE: 3645] RE: 3644] Breesh-Lock Heat Exchangers Weld overlay


Hi
Single layer 347 weld overlay by ESSC is good solution and you can also try
with Soudokay/Sandvik strip with High speed flux You should be able to
achieve 4.5 thk weld clad with top 3 mm undiluted chemistry of 347 It is
established process with nil disbanding. However if you want final weld
thickness of 5mm after machining better to go for Double layer where you
should get w/o thk of 7 mm and at least 2 mm M/cing allowance to take care
of distortion during welding

Hope this will solve your problem

Regards

Hegde P.B.

-----Original Message-----
From: materials-welding@googlegroups.com
[mailto:materials-welding@googlegroups.com] On Behalf Of GERING, Erwin
Sent: Friday, November 13, 2009 2:50 PM
To: materials-welding@googlegroups.com
Subject: [MW:3645] RE: 3644] Breesh-Lock Heat Exchangers Weld overlay


Hello Mr Singh,

Single layer strip cladding solution is possible for SS347 with ES and SA
process.
Depending on dimensions and requirements selection to be made :

SA-strip:
OERLIKON AST 300 - SUPRASTRIP 24 13LNb
OERLIKON AST 347 - SUPRASTRIP 24 13LNb

ES strip:
OERLIKON ELT 300 - SUPRASTRIP 21 11LNb (low speed)
OERLIKON ELT 300S - SUPRASTRIP 24 13LNb (high speed)
OERLIKON ELT 347-1 - SUPRASTRIP 19 9LNb (low speed)
 
In general the ES-strip cladding process can not garantue zero defects
(PT-check) after machining in the ovelap zone. SA strip cladding process
should be chosen in that case.
 
With kind regards,
Erwin GERING
AIR LIQUIDE WELDING


-----Oorspronkelijk bericht-----
Van: materials-welding@googlegroups.com
[mailto:materials-welding@googlegroups.com] Namens JASPAL SINGH
Verzonden: vrijdag 13 november 2009 6:03
Aan: Materials & Welding
Onderwerp: [MW:3644] Breesh-Lock Heat Exchangers Weld overlay


Dear all,

I have query regarding the Weld Overlay in Breesh Lock Heat
Exchanger.

As per specifications it is required to give SS347 Weld- overlay with
3mm undiluted chemistry . It is written that weld overlay shall be
lined & Faced. does it mean Strip cladding First then Machining.

Secondly is it possible to offer single layer solution for the same.

IS it required to machine the overlay in Breesh Lock Heat Exchanger.

Thanks in advance

Jaspal Singh


--~--~---------~--~----~------------~-------~--~----~
To post to this group, send email to materials-welding@googlegroups.com
To unsubscribe from this group, send email to materials-welding-unsubscribe@googlegroups.com
For more options, visit this group's bolg at http://materials-welding.blogspot.com/
The views expressed/exchnaged in this group are members personel views and meant for educational purposes only, Users must take their own decisions w.r.t. applicable code/standard/contract documents.
-~----------~----~----~----~------~----~------~--~---

No comments: