[MW:2006] Re: Copper#SS304L brazing

Is it must to do by brazing ? if TIG permissible try using  ER Cu Sn-A 2.00mmwire
Regards
SUNEEL GORE

--- On Wed, 22/4/09, PREM SHANKARDUTT NAUTIYAL <prem_nautiyal@rediffmail.com> wrote:

From: PREM SHANKARDUTT NAUTIYAL <prem_nautiyal@rediffmail.com>
Subject: [MW:2005] Copper#SS304L brazing
To: materials-welding@googlegroups.com
Date: Wednesday, 22 April, 2009, 9:00 AM

 
Dear friends

We are trying to braze a SS304L tube # Copper tube with OD=15mm and wall thickness 3mm. The joint is a simple square butt joint. Now we have tried torch brazing with following consumables:
L&T Eutectic 1601 flux + L&T 1601 filler wire.
This is a silver brazing filler wire with @ 40% silver,and balance Cu ,i.e.BAg-4 (EWAC 1601)
However we are not able to achieve torch brazing successfully.
We have even tried with Mathure Silver brazing filler wire and flux, but procedure has failed i.e weak joint.
Actually while brazing the filler material flows towards Copper side and does not flow towards SS304L side resulting in a weak joint and can be easily broken by a blow.
The joint also has to pass helium leak test.

Can anybody suggest suitable brazing procedure and technique.
I have read about furnace brazing but it is not practically possible in our job.
We only have the option of torch brazing.

Regards

Prem Nautiyal
Godrej,Mumbai
Cell: 9820313278
PREM S NAUTIYAL
CELL : 9820313278


Cricket on your mind? Visit the ultimate cricket website. Enter now! --~--~---------~--~----~------------~-------~--~----~
To post to this group, send email to materials-welding@googlegroups.com
To unsubscribe from this group, send email to materials-welding-unsubscribe@googlegroups.com
For more options, visit this group's bolg at http://materials-welding.blogspot.com/
The views expressed/exchnaged in this group are members personel views and meant for educational purposes only, Users must take their own decisions w.r.t. applicable code/standard/contract documents.
-~----------~----~----~----~------~----~------~--~---

By -

No comments:

Post a Comment

Subscribe to: Post Comments (Atom)

[MW:34916] Applicability of Impact requirement as per ASME B31.3

Dear All, Design code – ASME B31.3, Welding Code- ASME BPVC SEC IX Material  to be used used during Fabrication - SA 333Gr6 (P No.1 G...

  • Materails FAQs
    Q: What are equivalents for standard Q 235 B (and Q 235 A) for U-channels? ...
  • RE: [MW:5585] Buttering of weld joints
    Definition of buttering from ASME Section IX, QW/QB-492 Definitions:   Buttering:  the addition of material, by welding, on one or bot...
  • WELD AND WELDING SYMBOLS
    Section I. PRINT READING 3-1. GENERAL a. Drawings . Drawing or sketching is a universal language used to convey all necessary information to...