[MW:1795] Re: Polarity Vs Heat generation

+ve side heat will be more . 
Tagore 

On Sun, Mar 22, 2009 at 2:38 PM, Tirumala B N Tagore <tagore.tbn@gmail.com> wrote:


On Sun, Mar 22, 2009 at 9:22 AM, Muhammed Ibrahim <ibratech@gmail.com> wrote:

Hi members,
 
I would like to get a clarification in a matter. Is there any recomendation to use electrode -ve for overlay to get less dilution?. Is there any relation with electrode polarity and heat generation?.

Thanks & Regards
Muhammed Ibrahim PK





--~--~---------~--~----~------------~-------~--~----~
To post to this group, send email to materials-welding@googlegroups.com
To unsubscribe from this group, send email to materials-welding-unsubscribe@googlegroups.com
For more options, visit this group's bolg at http://materials-welding.blogspot.com/
The views expressed/exchnaged in this group are members personel views and meant for educational purposes only, Users must take their own decisions w.r.t. applicable code/standard/contract documents.
-~----------~----~----~----~------~----~------~--~---

No comments:

Re: [MW:34832] Inquiry about Single Bevel with Back Grinding

Dear Uday, As per your question that one is called with backing only,Simple both side you are welding it is backing with strip or without st...