[MW:1597] Re: 1593] FILLER WIRE FOR TIG WELDING AT 4.5K ( - 269 CENTIGRADE) TEMP.

Dear sir,

As per ASME SEC-II part C SFA-5.9 page No : 229 suggest ER316LMn

also ASME SEC-VIII DIV-1 UHA-51(a) 4,page No:207 suggest for lower
temp below -196 you should go for ER316L with ferrite content less
than 5 . if we want to use other than this filler wire you should go
for ASTM E 1820.

After refer above standard please reply me what filler wire should i use ?

regards

Hitesh Patel

On 2/17/09, tim.buyle@arcelormittal.com <tim.buyle@arcelormittal.com> wrote:
>
> Hello,
>
> You should look for an ER-308L (SFA 5.9) filler wire with a low ferrite
> content (WRC'92 calculation : between 4 and 6)
> Talk to your consumables supplier, to see if some other restrictions on
> the chemistry are necessary.
>
> Regards,
>
> Tim Buyle.
>
>
> -----Original Message-----
> From: materials-welding@googlegroups.com
> [mailto:materials-welding@googlegroups.com] On Behalf Of hitesh patel
> Sent: dinsdag 17 februari 2009 11:02
> To: materials-welding@googlegroups.com
> Subject: [MW:1593] FILLER WIRE FOR TIG WELDING AT 4.5K ( - 269
> CENTIGRADE) TEMP.
>
>
> DEAR FRIENDS,
>
> FOR SS304L TIG WELDING WHAT FILLER WIRE CAN USE AT 4.5K ( - 269
> CENTIGRADE) TEMP.
>
> ALSO FOR THIS WPS,PQR AT WHAT TEMP. I SHOULD DO IMPACT TEST & WHAT IS
> THE ACCEPTABLE LIMIT FOR IMPACT TEST OR LETARAL EXPANSION TEST
>
> PLS GIVE ME REPLY
>
> THANKS & REGARDS,
>
> HITESH PATEL
>
>
>
> ****
> This message and any attachment are confidential, intended solely for the use of the individual or entity to whom it is addressed and may be protected by professional secrecy or intellectual property rights.
> If you have received it by mistake, or are not the named recipient(s), please immediately notify the sender and delete the message. You are hereby notified that any unauthorized use, copying or dissemination of any or all information contained in this message is prohibited.
> Arcelormittal shall not be liable for the message if altered, falsified, or in case of error in the recipient.
> This message does not constitute any right or commitment for ArcelorMittal except when expressly agreed otherwise in writing in a separate agreement.
> ****
>
>
> >
>

--~--~---------~--~----~------------~-------~--~----~
To post to this group, send email to materials-welding@googlegroups.com
To unsubscribe from this group, send email to materials-welding-unsubscribe@googlegroups.com
For more options, visit this group's bolg at http://materials-welding.blogspot.com/
The views expressed/exchnaged in this group are members personel views and meant for educational purposes only, Users must take their own decisions w.r.t. applicable code/standard/contract documents.
-~----------~----~----~----~------~----~------~--~---

No comments:

[MW:34820] RE: 34813] Clarification in Rate of heating and cooling.

Hello,   Please see the response below.   Regards.   P. Goswami, P. Eng, IWE.   From: materials-welding@googlegroups.com <materials-weld...