Thursday, February 12, 2009

[MW:1559] RE: 1555] Re: 1553] Re: burn through

Dear Ali,

 

Its not excessive, it is just required “Penetration”. Excessive penetration will fall under “weld defect”

 

Regards.

 

C. K. Purohit

General Manager - QC

KNM Process Systems Sdn Bhd - Malaysia

 

HP No. : 6016-3376448


From: materials-welding@googlegroups.com [mailto:materials-welding@googlegroups.com] On Behalf Of Ali Asghari
Sent: Thursday, February 12, 2009 12:55 PM
To: materials-welding@googlegroups.com
Subject: [MW:1555] Re: 1553] Re: burn through

 

hi

realy ,melt through is excessive penetration?

best regard

 


From: Chaitanya Purohit <ck@knm-group.com>
To: materials-welding@googlegroups.com
Sent: Thursday, February 12, 2009 8:05:17 AM
Subject: [MW:1554] RE: 1553] Re: burn through

I do not agree with the interpretation of term “Melt Through” with Mr. César.

 

Melt Through is not a synonym for burn through. “Burn through” is the type of defect where the “Melt through” is the desired property for good weld. Melt through is considered as “Penetration” which we use during welding inspection. There shall be full penetration (no lack of penetration –LOP) if you interpret AWS correctly.

 

As correctly said if can not be seen visually but generally in UT , interpreters are putting as “No LOP Observed” which complies to AWS requirement stated. I am not the expert is AWS D1.1 and I am sure there are people in group who can through some light on this issue.  

 

Regards.

 

C. K. Purohit

General Manager - QC

KNM Process Systems Sdn Bhd - Malaysia

 

HP No. : 6016-3376448


From: materials-welding@googlegroups.com [mailto: materials-welding@googlegroups.com ] On Behalf Of César Alexis Viteri Pérez
Sent: Thursday, February 12, 2009 5:07 AM
To: materials-welding@googlegroups.com
Subject: [MW:1553] Re: burn thrugh

 

Burn trough is a nonstandard term for melt through.
 
"melt-through.- Visible root reinforcement in a jointwelded from one side." - AWS 3.0
 
I'm not a structural eng but for tubular k,y,t conections where the inspection inside the pipe is difficult is preferrable guarantee full penetration and fusion, may be a structural could give us a better explanation.
 
BR 
 

 


Date: Wed, 11 Feb 2009 04:11:46 -0800
From: asghariali@rocketmail.com
Subject: [MW:1550] burn thrugh
To: materials-welding@googlegroups.com

 

 

hi

melt through is excessive weld or burn through?

in aws d1.1 is written that"melt through is desirable in T,K,Y joint".(in 4.8.1).why?

thanks adv



</html





***DISCLAIMER NOTICE ***

"This email and any files transmitted with it is confidential and is intended only for the use of the recepient(s) named above. If you are not the intended recipient, any review, retransmission, dissemination, distribution, printing, copying or use the information contained in this message or any part thereof in other manner is strictly prohibited. If you receive this email in error, please notify the sender immediately by return email and delete the email and any of its attachments. Any personal views or opinions expressed by the sender shall be understood as neither given nor endorsed by KNM or any of the companies within the Group."









***DISCLAIMER NOTICE ***

"This email and any files transmitted with it is confidential and is intended only for the use of the recepient(s) named above. If you are not the intended recipient, any review, retransmission, dissemination, distribution, printing, copying or use the information contained in this message or any part thereof in other manner is strictly prohibited. If you receive this email in error, please notify the sender immediately by return email and delete the email and any of its attachments. Any personal views or opinions expressed by the sender shall be understood as neither given nor endorsed by KNM or any of the companies within the Group."




--~--~---------~--~----~------------~-------~--~----~
To post to this group, send email to materials-welding@googlegroups.com
To unsubscribe from this group, send email to materials-welding-unsubscribe@googlegroups.com
For more options, visit this group's bolg at http://materials-welding.blogspot.com/
The views expressed/exchnaged in this group are members personel views and meant for educational purposes only, Users must take their own decisions w.r.t. applicable code/standard/contract documents.
-~----------~----~----~----~------~----~------~--~---


No comments:

[MW:34820] RE: 34813] Clarification in Rate of heating and cooling.

Hello,   Please see the response below.   Regards.   P. Goswami, P. Eng, IWE.   From: materials-welding@googlegroups.com <materials-weld...